Firing temperature °C | Batch no | Bulk density (g/cm3) | Apparent porosity (%) | Water absorption (%) | Linear shrinkage |
---|---|---|---|---|---|
1140 | 1 | 2.12 | 15.15 | 7.15 | 7.53 |
2 | 2.07 | 10.86 | 5.25 | 6.60 | |
3 | 2.20 | 7.58 | 3.45 | 7.51 | |
4 | 2.29 | 7.0 | 3.06 | 7.56 | |
1160 | 1 | 2.27 | 13.43 | 5.92 | 6.80 |
2 | 2.29 | 11.14 | 4.86 | 6.48 | |
3 | 2.31 | 5.71 | 2.47 | 7.25 | |
4 | 2.23 | 7.19 | 3.22 | 7.79 | |
1180 | 1 | 2.20 | 11.63 | 5.29 | 7.68 |
2 | 2.25 | 10.0 | 4.40 | 6.79 | |
3 | 2.28 | 5.28 | 2.32 | 7.11 | |
4 | 2.30 | 5.42 | 2.36 | 7.48 | |
1200 | 1 | 2.23 | 8.37 | 3.75 | 8.24 |
2 | 2.23 | 6.29 | 2.73 | 7.13 | |
3 | 2.16 | 5.30 | 2.45 | 6.24 | |
4 | 2.19 | 5.66 | 2.59 | 6.55 | |
1220 | 1 | 2.29 | 7.79 | 3.40 | 8.65 |
2 | 2.24 | 3.83 | 1.71 | 7.49 | |
3 | 2.18 | 3.10 | 1.42 | 6.04 | |
4 | 2.26 | 2.31 | 1.02 | 7.17 | |
1240 | 1 | 2.28 | 7.40 | 3.25 | 8.42 |
2 | 2.30 | 3.58 | 1.56 | 7.43 | |
3 | 2.19 | 2.49 | 1.14 | 6.24 | |
4 | 2.19 | 2.95 | 1.35 | 7.27 | |
1260 | 1 | 2.37 | 5.58 | 2.35 | 8.91 |
2 | 2.30 | 2.84 | 1.24 | 7.14 | |
3 | 2.11 | 6.17 | 2.92 | 4.44 | |
4 | 2.15 | 4.90 | 2.28 | 5.22 | |
1280 | 1 | 2.36 | 5.0 | 2.15 | 8.68 |
2 | 2.20 | 1.56 | 0.72 | 6.25 | |
3 | 1.97 | 4.21 | 2.14 | 3.72 | |
4 | 2.08 | 4.93 | 2.38 | 4.73 |